CAS No.: 25608-12-2
Other Names: hand lay up FRP vehicle shell resin
MF: C3H5NO)n
EINECS No.: 208-750-2
Type: Synthetic Resin And Plastics
Brand Name: TIANMA
Model Number: TM-196, TM-196
Appearance: Transparent light yellow liquid
Packaging: metal barrel
Usage: hand lay up FRP vehicle shell resin
Net Weight: 220kg
Certificate: Msds
Storage Period: 90 days .but it's 30 days if add thixotropice accelerator
Storage Condition: Below 25℃ in dark
Keywords: hand lay up FRP vehicle shell resin
Place Of Origin: Jiangsu, China
Purity: 66-72
Brand: TIANMA
| Selling Units | : | ton |
| Package Type | : | metal barrel |
TM-196 general purpose UP Resin Product Description
TM-196 Unsaturated Polyester Resin is a general IG type resin with medium viscosity, good toughness and mechanical strength. It can be used instead of Xinyang 196 Unsaturated Resin. It is suitable for hand paste forming and surfacing FRP car shell, Marine parts and other FRP products.
1. liquid resin property：
| item | unit | standard | testing method |
| appearance | —— | transparent light yellow liquid | GB/T 8237.4.1.1 |
| viscosity | 25℃,Pa.S | 0.60~1.20 | GB/T 7193.1 |
| gel time | 25℃,min | 9.1~18.9 | GB/T 7193.6 |
| acid value | mgKOH/g | 17~25 | GB/T 2895 |
| solid content | % | 64~70 | GB/T 7193.3 |
gel time: 50% cyclohexanone Peroxide paste 4%; Curing Agent E1: 4%
casting body property(for reference)
| Item | Unit | Measured data | Testing method |
| Barcol hardness | —— | 46 | GB 3854—83 |
| distortion temperature | ℃ | 72 | GB 1634—04 |
| bending strength | Mpa | 120 | GB2570—95 |
| tensile strength | Mpa | 76 | GB2568—95 |
| elongation | % | 2.0 | GB2568—95 |
| Impact strength | KJ/M2 | 13 | GB2571—95 |
| Water absorption | % | 0.15 | GB1462—88 |
Notes:
1） casting body sample preparation method accord to GB 8237—87.
2） Curing system: Curing agent 55% MEKPO: 1%, accelerate E1: 2%.
3） Post cure: 60℃×2h +80℃×2h
FRP products property( for reference)
| item | unit | measured data | testing method |
| bending strength | MPa | 316 | GB/T2570—95 |
| bending modulus | MPa | 1.36×104 | GB/T2570—95 |
Notes:
1） FRP sample preparation method accord to GB 8237—87.
2）Curing system: curing agent 55% MEKPO: 2%, accelerate E1: 2%.
4） Post cure: 60℃×3h +110℃×3h
Recipe (for reference)
| Item | Parts by weight |
| TM-196 UP resin | 100 |
| Curing agent(55%MEKPO 50% cyclohexanone peroxide paste) | 2-4 |
| Accelerator E1 | 1-4(according to local temperature) |
Storage
Stored under 25℃ shelter,flame and heat isolated, 3 month shelf life.
Notes
1. High efficient colorless accelerate is prohibit to choose,will lead to finished product surface sticky phenomenon because of finished product poor curing, Fiberglass special accelerate is recommended.
2. If operated in high humidity or high temperature circumstance,finished product surface will also get easily sticky,proper percentage liquefied beeswax is recommended to be added
Packaging & Shipping
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now